tensile
Strength, min |
|
yield
Strength
(0.2%offset)
min or range |
|
elongation
In 4d |
reduction
Of area |
grade |
ksi |
mpa |
ksi |
mpa |
min.% |
min.% |
1 |
35 |
240 |
20 |
138 |
24 |
30 |
2 |
50 |
345 |
40 |
275 |
20 |
30 |
2h |
58 |
400 |
40 |
275 |
20 |
30 |
3 |
65 |
450 |
55 |
380 |
18 |
30 |
4 |
80 |
550 |
70 |
483 |
15 |
25 |
5 |
130 |
895 |
120 |
828 |
10 |
25 |
6 |
120 |
828 |
115 |
795 |
10 |
25 |
7 |
50 |
345 |
40 |
275 |
20 |
30 |
7h |
58 |
400 |
40 |
275 |
20 |
30 |
9 |
90 |
620 |
70 |
483 |
15 |
25 |
9i |
90 |
620 |
70 |
483 |
12 |
25 |
11 |
35 |
240 |
20 |
138 |
24 |
30 |
12 |
70 |
483 |
50 |
345 |
18 |
25 |
13 |
40 |
275 |
25 |
170 |
24 |
30 |
14 |
60 |
410 |
40 |
275 |
20 |
30 |
15 |
70 |
483 |
55 |
380 |
18 |
25 |
16 |
50 |
345 |
40 |
275 |
20 |
30 |
16h |
58 |
400 |
40 |
275 |
20 |
30 |
17 |
35 |
240 |
25 |
170 |
24 |
30 |
18 |
90 |
620 |
70 |
483 |
15 |
25 |
18i |
90 |
620 |
70 |
483 |
12 |
20 |
19ii |
115 |
793 |
110 |
759 |
15 |
25 |
19iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
19e |
165 |
1138 |
160 to 185 |
1104 to 1276 |
5 |
20 |
20ii |
115 |
793 |
110 |
759 |
15 |
25 |
20iii |
135 |
930 |
130 to 159 |
897 to 1096 |
10 |
20 |
20iv |
165 |
1138 |
160 to 185 |
1104 to1276 |
5 |
20 |
21ii |
115 |
793 |
110 |
759 |
15 |
35 |
21iii |
140 |
966 |
130 to 159 |
897 to 1096 |
10 |
30 |
21iv |
170 |
1172 |
160 to 185 |
1104 to 1276 |
8 |
20 |
23 |
120 |
828 |
110 |
759 |
10 |
15 |
23i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
25 |
24 |
130 |
895 |
120 |
828 |
10 |
25 |
25 |
130 |
895 |
120 |
828 |
10 |
25 |
26 |
50 |
345 |
40 |
275 |
20 |
30 |
27 |
35 |
240 |
25 |
170 |
24 |
30 |
28 |
90 |
620 |
70 |
483 |
15 |
25 |
28i |
90 |
620 |
70 |
483 |
12 |
20 |
29 |
120 |
828 |
110 |
759 |
10 |
25 |
29i |
120 |
828 |
110 |
759 |
7.5 v,6.0vi |
15 |
30 |
50 |
345 |
40 |
275 |
20 |
30 |
31 |
65 |
450 |
55 |
380 |
18 |
30 |
32 |
100 |
689 |
85 |
586 |
10 |
25 |
33 |
50 |
345 |
40 |
275 |
20 |
30 |
34 |
65 |
450 |
55 |
380 |
18 |
30 |
35 |
130 |
895 |
120 |
828 |
5 |
20 |
36 |
65 |
450 |
60 to 95 |
410 to 655 |
10 |
|
37 |
50 |
345 |
31 |
215 |
20 |
30 |
38 |
130 |
895 |
115 |
794 |
10 |
25 |
above
Properties apply to longitudinal sections up to 3 inch thickness
With maximum of 10 inch. Mechanical properties of larger
Sections shall be negotiated between the manufacturer and
Purchaser. |
i)
Properties for material in transformed-beta condition. |
ii)
Properties for solution treated condition. |
iii)
Properties for solution treated and aged condition-moderate
Strength (determined by aging temperature). |
iv)
Properties for solution treated and aged condition-high
Strength (determined by aging temperature). |
v)
For product section or wall thickness values < 1.0 in. |
vi)
For product section or wall thickness values_> 1.0 in. |
** While this information has
been compiled with care, it is for convenience and for reference
only and we assume no liability for any decisions based on the
content therein. it shall be your responsibility to ensure
that any information in this document or on our website meets your
specific requirements.
**